ASME 8.1焊接冲击取样 单工艺及组合工艺 是讨论，不是分享！大家积极参与讨论啊

fredwang

wxdh007 发表于 2021-4-23 18:16
你好，感谢回复我也是这么想的，焊缝金属的要分，热影响区不用

可是有人说

您说的是UG-84(h)(3)和UG-84(h)(5)吧？原来只看了UG-84(g)，没看(h)。好久不用冲击这部分内容，顾前不顾后，不记得要求了。确实如那位仁兄所言，焊缝和热影响区取样，要兼顾每一种方法。When qualifying a welding procedure with impact testing that employs multiple welding processes, or multiple sets of essential and supplementary essential variables for a
welding process, the welding procedure shall be qualified by testing separate sets of impact test specimens removed from the weld metal and heat-affected zone, as follows:
(-a) The requirements of (f) shall be met.
(-b) The requirements of (g) and (3) specifying the location, number, and orientation of test specimen sets to be removed for each welding process or set of variables

wxdh007

fredwang 发表于 2021-4-25 21:52
您说的是UG-84(h)(3)和UG-84(h)(5)吧？原来只看了UG-84(g)，没看(h)。好久不用冲击这部分内容，顾前不顾 ...

是的所以我现在也是赞成，haz也要按每种焊接方法或变素

对了还有，取样是否一定要从最后熔覆面开始算呢，您怎么看

wx_SA2JyhZA

ASME冲击试样距离表面的距离不是要求4/T吗？

wxdh007

wx_SA2JyhZA 发表于 2021-6-29 16:51
ASME冲击试样距离表面的距离不是要求4/T吗？

要看情况的，不是所有都是这样

wx_SA2JyhZA

wxdh007 发表于 2021-6-29 17:53
要看情况的，不是所有都是这样

您做冲击时，是在室温做的，还是在最低金属使用温度做的？

wxdh007

wx_SA2JyhZA 发表于 2021-6-30 16:46
您做冲击时，是在室温做的，还是在最低金属使用温度做的？

asme 是按最低设计温度，或者其他情况

wx_SA2JyhZA

wxdh007 发表于 2021-6-30 18:26
asme 是按最低设计温度，或者其他情况

现在遇到个问题，最低设计温度除了做试验，也可以说计算出来，但是计算方法不会，您了解这块吗？

yz123456

您好，是不是按最新标准考虑的，因为最新标准上面只分2种厚度情况
1.小于19mm 按之前不变
2.大于19mm 单面焊缝，2种焊接方法，哪怕厚度超过19mm，每种方法只取1组；双面焊时还是（单一焊接方法）2组，多种时，每种焊接方法分开，取样按每种焊接方法的厚度取。
是不是新标准更简单化

weijiazan

感谢分享学习了感谢分享学习了

justing

感谢分享~学习了!!