管件的开孔补强计算豁免

emperor620

以前一直都是意外标准的配件可以按照UG36(3)(a)补强计算豁免，但是发现在UW16 (f) standard fittings 有如下要求：
（3)(a) Fittings not exceeding NPS 3 (DN 80), as shown in Fig. UW-16.2, may be attached to vessels that are not subject to rapid fluctuations in pressure by a fillet weld deposited from the outside only without additional reinforcement other than is inherent in the fitting and its attachment to the vessel wall provided all of the following conditions are met:
(1) maximum vessel wall thickness of 38 in.(10 mm);
(2) the maximum size of the opening in the vessel is limited to the outside diameter of the attached pipe plus 34 in. (19 mm), but not greater than one-half of the vessel inside diameter
.........
现在都疑惑了，是不是UG36(3)(a)不能用于配件的补强豁免？ 在上述 UW16(f)（3）（a）规定了只能使用FIg.UW-16.2所示连接方式采用此条豁免补强，且后续还规定了壁厚不能超过10mm，按此理解，不是上述的连接方式或壁厚超过10mm的配件开孔必须计算是否需要补强了？如采用FIG UW16.1 X,Y,Z等连接方式？各位大侠在使用standard fitting 是如何处理的呢？

太阳之城

你理解错了，是在满足以下条款时。可以采用FIG.UW16.2 这种结构焊接，并且不用计算补强。和UG36不冲突

gbt8163

觉得太阳之城的解释是对的。

henny1284

觉得太阳之城的解释是对的
- 本文出自ASME中国制造，原文地址：http://www.asmecn.com/thread-7239-1-1.html

niuwa

同意楼上的意见，2楼是对的

saintcaptain

进来学习一下 啊                              

W.Y

又跟着楼主学习了下标准。收益很多！

emperor620

太阳之城 发表于 2013-9-11 07:23
你理解错了，是在满足以下条款时。可以采用FIG.UW16.2 这种结构焊接，并且不用计算补强。和UG36不冲突

是我理解错了，在UG36(3)(a)原文如下：
Openings in vessels not subject to rapid fluctuations in pressure do not require reinforcement other than
that inherent in the construction under the following conditions: (a) welded, brazed, and flued connections meeting the applicable rules and with a finished opening not larger than:
只要满足这个applicable rules 焊接结构可以使用此条进行补强计算豁免。当使用FIG.UW16.1的结构型式时，即可满足了UW15的焊缝强度要求以及UW16的最低焊缝要求 ，就可以使用UG36(3)(a)的补强计算豁免。不知道我的理解是否正确呢

Smile

2楼的理解正确，学习

太阳之城

emperor620 发表于 2013-9-11 11:14
是我理解错了，在UG36(3)(a)原文如下：
Openings in vessels not subject to rapid fluctuations in pre ...

这个我的理解是只要是满足UW-13(f)(3)(a)就可以不用另外的开口补强了。目前还不能确定两者有没有冲突。如果有人指出冲突的话。可能需要补强计算了。