5mm不锈钢的工艺评定问题，MDMT为-196°C

fredwang

条件如标题，在此条件下，PQR需要做冲击，6mm及以上的板不能覆盖，5mm及以下板取不了样，纠结良久，不知道各位有何良策。

fredwang

如果用壁厚5.54的不锈钢钢管，恐怕也取不了样吧。

lyklzy

根据 QW-451.1:
Thickness T of Test Coupon, Welded (mm):                 1.5 to 10 incl.
Range of Thickness T of Base Metal, Qualified (mm):  Min.  1.5    Max.   2T
6mm 及以上的板怎么不能覆盖 5mm 呢？只要不超过 10mm。

fredwang

lyklzy 发表于 2013-1-28 21:13
根据 QW-451.1:
Thickness T of Test Coupon, Welded (mm):                 1.5 to 10 incl.
Range of T ...

因为要冲击，适用QW-403.6.
QW-403.6 The minimum base metal thickness qualified is the thickness of the test coupon T or 5⁄8 in. (16 mm),whichever is less. However, where T is less than 1⁄4 in.(6 mm), the minimum thickness qualified is 1⁄2T. This variable does not apply when a WPS is qualified with a PWHT
above the upper transformation temperature or when an austenitic or P-No. 10H material is solution annealed after
welding.

firefly_chong

楼主在母材厚度选择上是正确的，的确在有冲击要求的情况下，不能超过6mm。建议采用5mm厚度母材做评定，冲击试验按照SA-370   22.2.2中采用小试样。

fredwang

据钢厂朋友透漏，不锈钢5mm的钢都是负偏差，这可真真如何是好。

lyklzy

根据 QW-403.6，------  However, where T is less than 1⁄4 in.(6 mm), the minimum thickness qualified is 1⁄2T.
焊接工艺评定用试板 6 mm，最小评定厚度是 3 mm （1/2T），最大评定厚度是 12 mm。

fredwang

lyklzy 发表于 2013-1-29 22:37
根据 QW-403.6，------  However, where T is less than 1⁄4 in.(6 mm), the minimum thickness qual ...

谢谢回复，但是根据这段文字，6mm所能覆盖的下限只能是6mm，而不是1/2T.

lyklzy

根据 QW-403.6，------  However, where T is less than 1⁄4 in.(6 mm), the minimum thickness qualified is 1⁄2T.
这段英文翻译成中文是“但如试件厚度 T 小于 1⁄4 in.(6 mm)时，最小评定厚度为 1⁄2T。
那么讲极端一点吧，试件厚度为 5.9mm ，所能覆盖的下限应该是 2.95 mm了吧。

lyklzy

至于 5.9mm 厚的试板怎么获得------机加工。