crazycn

经热处理后提高抗拉性能的铁素体钢主要指哪些？

lyklzy

见 ASME BPVC Section Ⅷ Division 1  2013 Edition
PART UHT
REQUIREMENTS FOR PRESSURE VESSELS CONSTRUCTED OF
FERRITIC STEELS WITH TENSILE PROPERTIES ENHANCED BY
HEAT TREATMENT
MATERIALS
UHT-5 GENERAL
(a) Steels covered by this Part subject to stress due to pressure
shall conform to one of the specifications given in Section II and
shall be limited to those listed in Table UHT-23.
                          Table UHT-23
Ferritic Steels With Properties Enhanced by Heat Treatment
     Spec. No.                       Type/Grade
       SA-333                         8
       SA-334                         8
       SA-353                         …
       SA-420                        WPL8
       SA-487                        4 Cl. B & E, CA6NM Cl. A
       SA-508                        4N Cl. 1 & 2
       SA-517                        A, B, E, F, J, P
       SA-522                        I
       SA-533                        B Cl. 3, D Cl. 3
       SA-543                        B, C
       SA-553                        I, II
       SA-592                        A, E, F
       SA-645                        A
       SA-724                        A, B, C
GENERAL NOTE: Maximum allowable stress
values in tension for the materials listed in
the above table are contained in Subpart 1
of Section II, Part D (see UG 23).

fgh222

感谢分享有关材料和标准

yuwen

八卷1分册UHT篇有说明

nufrats

八卷1分册UHT篇有说明，2漏厉害

crazycn

lyklzy 发表于 2015-6-24 15:07
见 ASME BPVC Section Ⅷ Division 1
                          Table UHT-23
Ferritic Steels With Pro ...

对境外牌号不熟，我再看看，谢谢！

zzcnhic

所有的铁素体钢经过热处理都可以提高抗拉强度

crazycn

zzcnhic 发表于 2015-6-28 21:22
所有的铁素体钢经过热处理都可以提高抗拉强度

主要哪种强化形式？细晶强化？

nokia3640

2楼是大神啊，膜拜一下。

zds2010

YANGSHI仰视央视了