关于ASME VIII-1卷UG-84, (5)(b)冲击温度的确定

过河卒子？

根据“UG-84，(-b) For Materials of Nominal Thickness Less Than 0.394 in. (10 mm). Where the largest obtainable Charpy V‐notch specimen has a width along the notch of at least 80% of the material nominal thickness, the Charpy test of such a specimen shall be conducted at a temperature not warmer than the minimum design metal temperature.34
Where the largest possible test specimen has a width along the notch of less than 80% of the material
nominal thickness, the test, for Table UCS-23 materials having specified minimum tensile strength of less than 95,000 psi (655 MPa), shall be conducted at a temperature lower than the minimum design metal temperature34 by an amount equal to the difference (referring to Table UG-84.2) between the temperature reduction corresponding to the actual material thickness and the temperature reduction corresponding to the Charpy specimen width actually tested.”的要求，对于公称壁厚小于10mm的材料，可获取试样缺口宽度小于材料公称厚度的80%时的试验温度确认，是否是低于最小设计温度的一个数值（实际壁厚降低的温度值和实际缺口宽度降低的温度值差值）。
例如
1) 最小设计温度为-29摄氏度
2) 实际壁厚为5mm(试验温度相比最小设计金属温度降低11摄氏度)
3) 夏比冲击试样缺口宽度为2.5mm，小于材料公称壁厚的80%(试验温度相比最小设计金属温度降低28摄氏度)
则试验温度=(-29)-[(-11)-(-28)]=-46摄氏度。
这样理解对吗？

本大风

是的，这部分主要考虑两部分温度降：1、实际试样厚度与标准试样厚度的差别 2、实际试样厚度与板厚的差别。这里的试样厚度即：a width along the notch，具体的讲为包含V型缺口的两表面的垂直距离。所谓的Subsize试样，唯一可以改变的尺寸就是厚度（示意图见ASTM E23-2007 Fig.A3.1）。
ASME VIII中冲击试验温度的调整都是以MDMT来确定的，而具体构件的MDMT在确定时已经考虑了板厚的因素，因此这里对于小厚度（t＜10mm）构件，实际冲击试样厚度小于0.8t时，其实只需要考虑，板厚和式实际冲击试样厚度尺寸差异带来的温度降，然而UG84.2表中的所有数据都是相对于10mm标准试样的温度降，因此才有了以上的规定。

tom6452

没错，你这个计算很正确。我是去年研究了这个问题，刚好请教过专家。所以你这个计算很正确，你理解到位。恭喜你。